THE GALVANIZING

Daniel Gheorghe LAKATOS, Mircea BEJAN

Abstract


This paper addresses some aspects of the process of wire galvanizing, with an emphasis on their zinc coating treatment. After producing wire by cold or hot drawing, the resulting structure consists of highly elongated crystals forming on the main direction. This structure influences the quality of deposited zinc layer and also the adhesion to the base material. In this case, the patent is strictly required for wire diameters up to 8-9 mm, because changing the crystalline structure helps to a much better grip of the coated zinc on the superficial layer, to the steel.

Key words: galvanizing, patent, wires, tensions, corrosion

Full Text:

PDF

References


Bejan, M., Recenzii într-o carte, Editura AGIR, București 2003

Lakatos, D., Zincarea termică – O tehnologie modernă, Știință și inginerie, volumul 20, pag. 473-478, Editura AGIR, București, 2010

Asociația Naţională a Zincatorilor, Zincare Termică – fișe de informare, Cluj Napoca, 2011

Matochkin, V.A., Heat treatment and surface preparation of high-carbon wire rod in drawing, Chemistry and materials science, vol 37, Number 6, pag 540-542, SpringerLink, 2007

Vermeşan, H., Mudura, P., Vermeşan, G., Berar, A., Bazele teoretice ale tratamentelor termice, Editura Universităţii din Oradea, Oradea, 2002

Navaei Alvar, E., Aghazadeh Mohandesi, J., Fatigue damage accumulation in cold-drawn patented steel wire under variable loading, Materials and Design, vol.31, issue 4, Elsevier journal, pag. 2018-2024, 2010

Verdejo Valls,V., Angeles Perez Alarco, M., Pilar Lino Sorli, M., Scheduling in a continuous galvanizing line, Computers & operations reserch, vol 36, pag 280-296, ScienceDirect, 2009

http://www.cnhbfuxing.en.made-in-china.com

http:// galvinfo.com

http:// zincworld.org

http:// zincare.eu


Refbacks

  • There are currently no refbacks.


JOURNAL INDEXED IN :